| Title |
Fracture Toughness of Directionally Solidified TiAl-Nb Alloys Containing Si and C |
| Authors |
김성용(Kim Seong Yong); 오명훈(O Myeong Hun); 위당문(Wi Dang Mun) |
| ISSN |
1738-8228(ISSN), 2288-8241(eISSN) |
| Keywords |
TiA1; Directional solidification; Lamellar microstructure; Fracture toughness; Lamellar orientation |
| Abstract |
The microstructure and mechanical properties of directional solidified Ti-47Al-3Nb, Ti-47Al-3Nb-0.2Si- 0.1C, Ti-47Al-3Nb-0.3Si-0.2C alloys were investigated. It was found that the lamellar thickness of Si and C doped alloys was fine and uniform, and little or no precipitates were found. Room temperature yield stress increased rapidly with increasing Si and C contents due to fine lamellar distribution and solid solution hardening. However, fracture toughness of type I specimens of the alloys decreased slightly with increasing Si and C contents. It was considered that α2 volume fraction decreased with increasing Si and C contents so that the delamination-type separation was decreased which contributes the high resistance of crack propagation for type Ⅰ specimens. Furthermore, fracture toughness of Ti-47Al-3Nb-0.2Si-0.1C alloy specimens with type Ⅰ orientation, polycrystalline form, and with type Ⅲ orientation increased in order of type Ⅲ, polycrystal and type Ⅰ. These results are discussed and the ability to obtain a respectable combination of strength and toughness through Si and C addition to a TiAl-Nb alloy produced by directional solidification is demonstrated. |