Fracture Characteristics of Flame Thermal Shock in PSZ/NiCrAlY FGM |
| Authors |
송준희(Jun Hee Song); 문상돈(Sang Don Mun) |
| DOI |
https://doi.org/10.3365/KJMM.2010.48.08.775 |
| ISSN |
1738-8228(ISSN), 2288-8241(eISSN) |
| Keywords |
functionally graded materials; FGM; powder processing; fracture; flame test; composites |
| Abstract |
Functionally graded materials (FGM) of PSZ/NiCrAlY on Inconel substrate were fabricated by detonation gun spraying method. A thick ceramic layer generally has a high thermal barrier effect however, because failure often occurs, the use of an FGM layer gives an advantage in thermal property. During the thermal shock test, micro fracture processes were detected by the AE method. Also, the thermal shock test was performed for NFGM, FGM and the changed FGM in the layered composition profile. It was found through AE testing and the observation of fracture surface that FGM was superior to NFGM in thermal shock properties. The linear or metal-rich type FGM in composition profile had the best resisting property among the FGM. It was found that the controlled composition profile of the graded layers had better thermal properties. |