Interlaminar Fracture Toughness of GFRP Composites for Insulating Structure of Magnet System |
| Authors |
송준희(Jun Hee Song); 김학근(Hak Kun Kim); 김연직(Yon Jig Kim) |
| DOI |
https://doi.org/10.3365/KJMM.2011.49.10.754 |
| ISSN |
1738-8228(ISSN), 2288-8241(eISSN) |
| Keywords |
composites; fracture toughness; mechanical properties; GFRP |
| Abstract |
In this study, the interlaminar fracture behaviors of laminated GFRP composites were investigated, and the results could be used for damage tolerance design based on fracture mechanics. Three types of laminated GFRP composites that can be used as high voltage insulating materials in magnet systems were fabricated in order to study the interlaminar fracture behavior according to the molding process. The values of interlaminar fracture toughness for the VPI, prepreg, and HPL laminate were 1.9 MPa · 1/2, 1.7 MPa · 1/2, and 2.2 MPa · 1/2, respectively. HPL laminate showed the best fracture resistance. The failure modes of HPL and VPI were similar to that of an adhesive joint, and prepreg laminates showed partial cohesive failure mode due to internal voids. |